The Effect of Bioglass Coating on Microshear Bond Strength of Resin Cement to Zirconia.

Objectives: Durable bonding to zirconia is a challenging issue in dentistry. This study aimed to assess the effect of bioglass coating of zirconia on the microshear bond strength of resin cement to zirconia and to study the effect of thermocycling on this bond. Materials and Methods: This in-vitro experimental study was conducted on 60 yttria-stabilized tetragonal zirconia blocks in six groups (N=10) based on surface pretreatment and thermocycling. Surface pretreatments included no treatment control, alumina particle abrasion, and bioglass-coating of zirconia. Resin bonding was performed with Panavia F2.0 cements. Then, half of the specimens underwent a 24-hour incubation in 37°C water, while the other half were subjected to thermocycling (12000 cycles, 5-55°C, 60s for each batch) following the same incubation period. Subsequently, the microshear bond strength of the specimens was measured. Additionally, one block from each group was subjected to scanning electron microscopy and X-ray diffraction. The data were analyzed using Kruskal-Wallis and Mann-Whitney U tests. Results: There was a significant difference between the bond strength values of different groups (P<0.001). Alumina particle abrasion and bioglass coating equally increased the bond strength compared to the untreated control group (P<0.001). Thermocycling caused significant decreases in bond strength in all the groups (P<0.001); however, the bond strength value of the thermocycled bioglass-coated group was significantly higher than that reported for the thermocycled alumina particle abraded group (P=0.015). Conclusion: Despite the decrease in the bond strength values after thermocycling, the long-term efficacy of the bioglass coating of zirconia was promising.

Comparison of Three Different Orthodontic Adhesives Bonded to Metallic and Ceramic Brackets: SEM and SEM/EDX Analysis (In Vitro Study).

Objectives: To compare three different orthodontic adhesives (Transbond XT Light Cure Adhesive, Heliosit Orthodontic, Fuji Ortho LC) bonded to two types of orthodontic brackets: ceramic brackets (Fascination Roth 0.22) and metallic brackets (Topic Roth 0.22, Dentaurum). Materials and methods: The study was performed on 18 human teeth (6 for each adhesive). The prepared teeth were divided into three groups according to the examination time. Subsequently, they were observed after 1, 2 and 3 weeks following bonding. After the experimental procedure, the teeth samples were cut in half along the longitudinal axis in the vestibulo-oral direction, fixed with conductive carbon cement, placed in a high-vacuum evaporator and then coated with carbon. One half of each sample was observed under a Field-emission gun scanning electron microscope (FEG-SEM Hitachi SU 8030, Japan), while on the second half of the samples qualitative (X-ray line-scans) and semi-quantitative point X-ray energy dispersive analyses (EDX) were performed with Thermo Noran (USA) NSS System 7, equipped with Ultra Dry detector (30 mm2 window). Results: Transbond XT had an ideal bond with the enamel and the bracket base, with rare presence of microgaps and cracks in the enamel. Heliosit Orthodontic demonstrated a better bond relationship with the bracket base than the enamel, whereas in the latter the presence of microgaps in the bond was observed. The microphotographs of Fuji Ortho LC demonstrated many cracks inside the adhesive, and some of them continued to move forward into the enamel surface. Therefore, an impression of a very solid bond relationship with the enamel exists, with cracks being present in the enamel surface and never at the enamel-adhesive interface. Microgaps also appeared at the bracket-adhesive interface. Conclusion: Transbond XT is a highly filled composite resin and is an ideal orthodontic adhesive in each aspect examined, with an ideal enamel-adhesive and bracket-adhesive interface. Heliosit Orthodontic provides better bracket-adhesive interface compared to the enamel. Fuji Ortho LC as a solid resin-modified GIC provides a better enamel-adhesive interface, compared to the bracket base.

Influence of silver fluoride plus potassium iodine on adhesive properties of primary carious dentin-resin interface: An in vitro study.

This paper evaluated the influence of different protocols of silver fluoride (SF) pretreatment of artificial carious lesions on the adhesive interface of composite resin restorations and remineralization of deciduous dentin compared to silver diamine fluoride (SDF). Sixty-four deciduous molar teeth were randomly divided into 8 groups (n = 8) according to the restoration time (immediately - IM; 30 days after SDF/SF treatment - 30 D) and treatment before restoration (SDF 38 %; SDF 38 % + potassium iodide - KI; SF 38 %; SF 38 % +KI). After SDF/SF application, teeth in the IM group were restored with self-etch universal adhesive system/composite resin. Samples in the 30D groups were stored in artificial saliva (37 °C) for 30 days before receiving the same restoring protocol. Beams were obtained from all groups and subjected to bond strength tests (µTBS), ultrastructural qualitative analysis (FEG) and mineral analysis (SEM/EDX; Micro-Raman spectroscopy). The µTBS data were subjected to three-factor ANOVA and multiple comparisons (Holm-Sidak method). Bond strength values (MPa) for IM groups were 16.9 ± 2.7 (SDF); 17.6 ± 3.5 (SDF + KI); 16.8 ± 5.5 (SF); 18.4 ± 4.1 (SF + KI); and 14.9 ± 4.2 (SDF); 16.0 ± 5.4 (SDF + KI); 14.1 ± 3.6(SF); 16.4 ± 5.4 (SF + KI) for 30D groups. Bond strength wasn't influenced by the moment of restoration (IM or 30D); the use of KI didn't alter adhesion characteristics; SDF/SF solutions resulted in similar adhesive strength; calcium and phosphate expressions were identified at the interfaces on IM and 30D moments. However, 30D presented qualitative increase in these ions, compatible with remineralization. It was concluded that the adhesion of composite resin restorations in artificial caries lesions of deciduous teeth treated with SDF (38 %) and SF (38 %) had similar effects in vitro; the use of KI or the moment when restorations were accomplished did not influence the adhesion and all tested protocols promoted remineralization of carious dentin.

Clinical evaluation of posterior restorations over wet and dry dentin using an etch-and-rinse adhesive: A 36-month randomized clinical trial.

OBJECTIVES: To evaluate the clinical performance of posterior restorations over wet and dry dentin with an etch-and-rinse adhesive after 36 months of clinical service. METHODS: Forty-five participants were recruited, each one had at least two posterior teeth that needed restoration. Ninety restorations were placed on Class I or Class II cavities. For the restoration protocol, a simplified etch-and-rinse adhesive (Adper Single Bond 2) was applied over wet (WD) or dry dentin (DD) and later restored with a bulk-fill composite (Filtek Bulk Fill) under rubber dam isolation. Each restoration was evaluated using the World Dental Federation (FDI) criteria after 6, 12, and 36 months of clinical service, regarding the following principal restoration characteristics: postoperative sensitivity, marginal discoloration, marginal adaptation, fracture of material and retention, and recurrence of caries. Kruskal Wallis analysis of variance rank (α = 0.05) and Kaplan-Meier survival analysis were used for statistical analysis. RESULTS: After 36 months of clinical evaluation, no significant difference between groups was observed in each FDI criterion (p > 0.05). Twenty restorations (WD=10, DD=10) showed minor marginal staining, and twenty-two restorations (WD=11, DD=11) presented small marginal adaptation defects (p > 0.05). Four restorations were lost (WD = 2, DD = 2) and the fracture rates (95% confidence interval) were 94.9% for each one, without significant difference between wet and dry dentin (p > 0.05). SIGNIFICANCE: The degree of dentin moisture does not seem to affect the clinical performance of a simplified etch-and-rinse adhesive in posterior restorations when the adhesive is applied vigorously over the dentine surface.

Multi-Parameter Characterization of HEMA/BPA-free 1- and 2-step Universal Adhesives Bonded to Dentin.

PURPOSE: This study aimed to investigate the bonding effectiveness of two HEMA/BPA-free universal adhesives (UAs) to flat dentin, to characterize their adhesive-dentin interfacial ultrastructure, and to measure their water sorption (Wsp), water solubility (Wsl), and hydrophobicity. MATERIALS AND METHODS: The immediate and aged (50,000 thermocycles) microtensile bond strength (µTBS) to flat dentin of the HEMA/BPA-free UAs Healbond Max (HbMax; Elsodent) and Healbond MP (HbMP; Elsodent) as well as the reference adhesives OptiBond FL (Opti-FL; Kerr), Clearfil SE Bond 2 (C-SE2; Kuraray Noritake), and Scotchbond Universal (SBU; 3M Oral Care) was measured. The adhesive-dentin interfaces of HbMax and HbMP were characterized by TEM. Wsp and Wsl of all adhesive resins and of the primer/adhesive resin mixtures of HbMax, Opti-FL, and C-SE2 were measured. Hydrophobicity was determined by measuring the contact angle of water dropped on adhesive-treated dentin. RESULTS: In terms of µTBS, HbMax and HbMP performed statistically similarly to Opti-FL and C-SE2, but outperformed SBU. Aging only significantly reduced the µTBS of SBU when applied in E&R bonding mode. TEM revealed typical E&R and SE hybrid-layer ultrastructures at dentin, while electron-lucent globules of unknown origin, differing in size and shape, were observed within the adhesive resin of HbMP and even more frequently in that of HbMax. Higher Wsp was measured for the primer/adhesive resin mixtures than for the adhesive resins. Opti-FL was more hydrophobic than all other adhesives tested. CONCLUSION: The HEMA/BPA-free UAs bonded durably to flat dentin with bond strengths comparable to those of the gold-standard E&R/SE adhesives and superior to that of the HEMA/BPA-containing 1-step UA.

Multifunctional Dental Adhesives Formulated with Silane-Coated Magnetic Fe3O4@m-SiO2 Core-Shell Particles to Counteract Adhesive Interfacial Breakdown.

The process of bonding to dentin is complex and dynamic, greatly impacting the longevity of dental restorations. The tooth/dental material interface is degraded by bacterial acids, matrix metalloproteinases (MMPs), and hydrolysis. As a result, bonded dental restorations face reduced longevity due to adhesive interfacial breakdown, leading to leakage, tooth pain, recurrent caries, and costly restoration replacements. To address this issue, we synthesized and characterized a multifunctional magnetic platform, CHX@SiQuac@Fe3O4@m-SiO2, to provide several beneficial functions. The platform comprises Fe3O4 microparticles and chlorhexidine (CHX) encapsulated within mesoporous silica, which was silanized by an antibacterial quaternary ammonium silane (SiQuac). This platform simultaneously targets bacterial inhibition, stability of the hybrid layer, and enhanced filler infiltration by magnetic motion. Comprehensive experiments include X-ray diffraction, FT-IR, VSM, EDS, N2 adsorption-desorption (BET), transmission electron microscopy, scanning electron microscopy, thermogravimetric analysis, and UV-vis spectroscopy. Then, CHX@SiQuac@Fe3O4@m-SiO2 was incorporated into an experimental adhesive resin for dental bonding restorations, followed by immediate and long-term antibacterial assessment, cytotoxicity evaluation, and mechanical and bonding performance. The results confirmed the multifunctional nature of CHX@SiQuac@Fe3O4@m-SiO2. This work outlined a roadmap for (1) designing and tuning an adhesive formulation containing the new platform CHX@SiQuac@Fe3O4@m-SiO2; (2) assessing microtensile bond strength to dentin using a clinically relevant model of simulated hydrostatic pulpal pressure; and (3) investigating the antibacterial outcome performance of the particles when embedded into the formulated adhesives over time. The results showed that at 4 wt % of CHX@SiQuac@Fe3O4@m-SiO2-doped adhesive under the guided magnetic field, the bond strength increased by 28%. CHX@SiQuac@Fe3O4@m-SiO2 enhanced dentin adhesion in the magnetic guide bonding process without altering adhesive properties or causing cytotoxicity. This finding presents a promising method for strengthening the tooth/dental material interface's stability and extending the bonded restorations' lifespan.

Influence of ceramic thickness and dental substrate on the survival rate and failure load of non-retentive occlusal veneers after fatigue.

OBJECTIVE: To investigate the effect of ceramic thickness and dental substrate (enamel vs. dentin/enamel) on the survival rate and failure load of non-retentive occlusal veneers. MATERIALS AND METHODS: Human maxillary molars (n = 60) were divided into five test-groups (n = 12). The groups (named DE-1.5, DE-1.0, DE-0.5, E-1.0, E-0.5) differed in their dental substrate (E = enamel, DE = dentin/enamel) and restoration thickness (standard: 1.5 mm, thin: 1.0 mm, ultrathin: 0.5 mm). All teeth were prepared for non-retentive monolithic lithium-disilicate occlusal veneers (IPS e.max Press, Ivoclar). Restorations were adhesively cemented (Syntac Classic/Variolink II, Ivoclar) and exposed to thermomechanical fatigue (1.2 million cycles, 1.6 Hz, 49 N/ 5-55°C). Single load to failure was performed using a universal testing-machine. A linear-regression model was applied, pairwise comparisons used the Student-Newman-Keuls method (p < 0.05). RESULTS: Three dentin-based occlusal veneers (one DE-1.0, two DE-0.5) revealed cracks after fatigue exposure, which corresponds to an overall-survival rate of 95%. Load to failure resulted in the following ranking: 2142 N(DE-0.5) > 2105 N(E-1.0) > 2075 N(E-0.5) > 1440 N(DE-1.5) > 1430 N(DE-1.0). Thin (E-1.0) and ultrathin enamel-based occlusal veneers (E-0.5) revealed high failure loads and surpassed the standard thickness dentin-based veneers (DE-1.5) significantly (p = 0.044, p = 0.022). CONCLUSION: All tested monolithic lithium disilicate occlusal veneers obtained failure loads above physiological chewing forces. Thin and ultrathin enamel-based occlusal veneers outperformed the standard thick dentin-based occlusal veneers. CLINICAL SIGNIFICANCE: Minimally invasive enamel-based occlusal veneer restorations with non-retentive preparation design may serve as a conservative treatment option.

Adhesive Bond Strength of Restorative Materials to Caries-Affected Dentin Treated with Antimicrobial Photodynamic Therapy: A Systematic Review and Meta-Analysis.

Objective: This systematic review aimed to evaluate the adhesive bond strength of restorative materials to caries-affected dentin (CAD) treated with antimicrobial photodynamic therapy (aPDT) in comparison with conventional chemical disinfectants. Methods: Three databases, including the Web of Science, Scopus, and PubMed, were searched to address the focused question: "What is the effect of aPDT compared to conventional chemical disinfection techniques on the adhesive bond strength of restorative materials to CAD?." Search keywords included "dentin*" "adhes bond*" "caries-affected dentin" "photodynamic "photochemotherapy" "photosensitizing agent" "phototherapy" "photoradiation" "laser" "light activated" "photoactivated." A fixed-effects model was used in each meta-analysis and the inverse variance was used to calculate the standard mean difference (SMD). For evaluating the statistical heterogeneity, the Cochrane's Q test and the I2 statistics were used. The risk of bias was evaluated based on the Cochrane Collaboration's tool. Results: Fourteen studies were included in the qualitative as well as quantitative analysis. The results of the meta-analyses exhibited an SMD of 2.38% [95% confidence interval (CI): 2.03-2.73; p < 0.00001], indicating a statistically significant difference in the shear bond strength scores between the tested group (samples treated with aPDT) and the control group (i.e., favoring the sound dentin and/or conventional chemical disinfectants). Contrarily, an SMD of -1.46% (95% CI: -2.04 to -0.88; p < 0.00001) and -0.37% (95% CI: -0.70 to -0.03; p = 0.03) was observed, indicating a statistically significant difference in the microtensile bond strength (µTBS), as well as microleakage scores between the tested group (favoring the samples treated with aPDT) and the control group (i.e., sound dentin and/or conventional chemical disinfectants). Conclusions: Adhesive bond strength of restorative materials to CAD treated with conventional chemical disinfectants showed superior outcomes compared to photodynamic therapy (aPDT).

Cytotoxicity evaluation, antibacterial effect, and degree of conversion of QAM-containing adhesives

Abstract The aim of this study was to evaluate the influence of adding quaternary ammonium methacrylates (QAMs) to experimental adhesives by assessing the degree of conversion (DC), cytotoxicity against keratinocytes and fibroblasts, and antibacterial activity against biofilm formation. Two QAMs were added to an experimental adhesive: dimethylaminododecyl methacrylate bromododecane (DMADDM) or dimethylaminododecyl methacrylate bromohexadecane (DMAHDM) at three concentrations each: 1, 2.5, and 5 wt.%. Experimental adhesive without QAMs (control group) and commercially available Transbond XT Primer (3M Unitek, Monrovia, California, USA) were used for comparisons. The adhesives were tested for DC, cytotoxicity against keratinocytes and fibroblasts, and antibacterial activity against biofilm formation. DC, cytotoxicity against fibroblasts, and antibacterial activity were analyzed using one-way ANOVA and Tukey's multiple comparisons. Cytotoxicity against keratinocytes was evaluated using the Kruskal Wallis and Dunn's post-hoc (α = 5%) tests. Transbond showed lower DC as compared to 5% DMAHDM, 1% DMADDM, and 5% DMADDM (p < 0.05). However, all groups presented proper DC when compared to commercial adhesives in the literature. In the evaluation of cytotoxicity against keratinocytes, Transbond induced higher viability than 2.5 wt.% groups (p < 0.05). Against fibroblasts, Transbond induced higher viability as compared to 5 wt.% groups (p < 0.05). DMAHDM at 5 wt.% reduced biofilm formation when compared to all the other groups (p < 0.05). Despite their cytotoxic effect against keratinocytes, gingival fibroblasts showed higher viability. DMAHDM at 5 wt.% decreased Streptococcus mutans viability. The incorporation of DMAHDM at 5 wt.% may be a strategy for reducing the development of white spot lesions.

Mechanical behavior of endodontically treated teeth: A three-dimensional finite element analysis using displacement vector.

PURPOSE: This study aimed to analyze the effects of core materials, remaining tooth structures, and interfacial bonding on stress distribution in endodontically treated teeth using finite element analysis (FEA). MATERIALS AND METHODS: Three-dimensional FEA was conducted using a reverse engineering technique based on maxillary premolars scanned by micro-computed tomography. Six models were generated with or without ferrules and with one of the following three abutment systems: metal core, resin core, or resin core with fiber posts. In each model, bonding and debonding were assumed in the dentin and surrounding structures: bonded and debonded models. The maximum principal stress values were recorded, and stress distribution of the entire restored teeth and dentin was generated. Furthermore, the distribution of the displacement vector of the debonded models was generated. RESULTS: In comparing the bonded and debonded models, the debonded models showed larger values for tensile stresses than those in bonded models for all abutment models. The models without ferrules rotated around the center of the abutment, whereas those with ferrules did not show remarkable displacement in the analysis. CONCLUSION: FEA assuming fracture of adhesive interface proved to be an effective method to clarify the significance of ferrules. It prevents stress concentration in dentin by reducing the rotation of the abutment, even when the adhesive fails.

Improving the Antibacterial Properties of Dental Bonding Materials Loaded with Silver Compounds.

Biofilm accumulation, the appearance of white spot lesions and the development of secondary caries are the main complications in orthodontic patients. A promising approach to fight this situation is the development of adhesive cements with improved antibacterial properties. The aim of the present study was to evaluate the possibility of improving the antibacterial properties of glass ionomer cements by incorporating different types of antimicrobial compounds without altering their physical and mechanical properties. Different concentrations of silver carbonate (SC) and an inorganic glass with encapsulated silver were added to the glass ionomer cement, as well as chitosan, to achieve synergistic antibacterial activity. Variations in the antibacterial capacity were evaluated using the agar diffusion test; the potential alteration of the physical and mechanical properties of the material was analyzed by the shear bond strength test. SEM characterization and colorimetric evaluation were also conducted. Samples of SC up to 1% and inorganic glass with encapsulated silver up to 5% showed significant improvement in their antibacterial ability without compromising shear strength. The highest antimicrobial activity was observed for Lactobacillus acidophilus, with inhibition zones of 3.8 and 3.1 mm for SC and inorganic glass, respectively. The characterization of the samples did not detect any major structural changes between the different samples. The only group that underwent a noticeable color change was the group with SC. The results show that the incorporation of silver carbonate and inorganic glass with encapsulated silver provided the glass ionomer cement with an antibacterial capacity without compromising the bond strength and without modifying the structure of the material.

Effect of Hydrofluoric Acid Concentration on Bond Strength to Glass-Ceramics: A Systematic Review and Meta-Analysis of In-Vitro Studies.

PURPOSE: To conduct a systematic review and meta-analysis of in-vitro bond strength to glass-ceramics using hydrofluoric acid (HF) at lower (<5%) and higher (>5%) concentrations ([HF]) to treat ceramic surfaces. METHODS: Systematic searches were carried out in PubMed, Scopus, LILACS, and Web of Science for articles published through July 2021, and a meta-analysis was performed to estimate the combined effect by comparing the differences between the standardized means of the bond strengths of the evaluated materials. RESULTS: In total, 943 articles were found, of which 17 studies were selected for qualitative analysis and 12 for quantitative analysis. The bond strength to glass-ceramics using 4% to 5% HF did not differ from that using 7% to 10% HF for the following HF etching times and glass-ceramic materials: 20 s for lithium-disilicate (Z = 0.65, p = 0.51), 60 s for feldspathic (Z = 0.53, p = 0.60), and 60 s for leucite (Z = 0.72, p = 0.35). CONCLUSION: The lower concentration HF (<5%) etchant is a reliable surface treatment for adhesive bonding to glass-ceramics with satisfactory bond strength in short-term evaluations.

The capacity of conservative preparations for lithium disilicate glass-ceramic laminates luted with different resin cements to mask different substrate shades: A minimally invasive esthetic approach.

OBJECTIVE: Demonstrate the ability of 0.5 mm thickness lithium disilicate laminates associated with resin cement to mask different substrate saturations. METHODS: 60 specimens (n = 5) were prepared with CAD/CAM lithium disilicate glass-ceramic IPS e.max CAD, 0.5 mm thick, in three degrees of translucency (HT, MT and LT); cemented by Variolink Esthetic LC Light+ (L) and Neutral (N) on composite resin substrates A1 and A4 shades. Color measurements were performed by a spectrophotometer (CM-3700d -Konica Minolta). The L*, a*, b* parameters of the tri-layer structure (laminate/ resin cement/ substrate) were used to calculate color difference ( ∆ E 00 $$ \Delta {\mathrm{E}}_{00} $$ ) by CIEDE2000 formula and Translucency Parameter ( TP 00 $$ {TP}_{00} $$ ). This study adopted ∆ E 00 $$ \Delta {\mathrm{E}}_{00} $$ = 0.8, as perceptibility threshold (PT), and ∆ E 00 $$ \Delta {\mathrm{E}}_{00} $$ = 1.8, as acceptability threshold (AT). Statistical analyses were performed by one-way ANOVA and Tukey tests (a = 0.05). RESULTS: Color difference between resin cement shades showed statistical differences (p < 0.0001) and ∆ E 00 $$ \Delta {\mathrm{E}}_{00} $$ > 1.8 for all groups. Color difference between substrates saturations showed a significant statistical difference (p < 0.0001) and ∆ E 00 $$ \Delta {\mathrm{E}}_{00} $$ values above AT for all groups. The TP 00 $$ {TP}_{00} $$ demonstrated significant statistical differences (p < 0.0001). The LTL combination, the opaquest set, showed the smallest ∆ E 00 $$ \Delta {\mathrm{E}}_{00} $$ values between substrate shades differences, however, above AT. CONCLUSION: The translucency of the lithium disilicate, the substrate saturation and the resin cement opacity influenced final color of restoration. The ceramic translucency impact on final color was reduced by opaque resin cement. Furthermore, the LT lithium disilicate and the Light+ resin cement reduced the translucency of the restoration, contributing to mask saturated substrate. CLINICAL RELEVANCE: This study shows the influence of conservative lithium disilicate laminates with different degrees of translucency associated with resin cement on final color of saturated substrate restorations. A minimally invasive esthetic protocol for masking substrates is demonstrated by associating low translucency ceramic laminates and opaque resin cement.

Influence of universal adhesives and silane coupling primer on bonding performance to CAD-CAM resin-based composites: A laboratory investigation.

OBJECTIVE: Obtaining strong resin bonds to computer-aided design and computer-aided manufacturing (CAD-CAM) resin-based composites with dispersed fillers (CCRBCs) poses a challenge. Therefore, this study aimed to assess the effect of three universal adhesives and a two-component silane coupling agent on the shear bond strength to three (CCRBCs). MATERIALS AND METHODS: Eight hundred and sixty-four specimens of Brilliant Crios, Lava Ultimate, and Tetric CAD were polished or grit blasted, bonded with Adhese Universal DC, One Coat 7 Universal (OC7), and Scotchbond Universal Plus Adhesive (SBU) with or without a silane primer. Shear bond strength was measured after 24 h and 10,000 thermocycles. Linear regressions were performed (α = 0.05). RESULTS: After thermocycling, bond strengths were similar for the universal adhesives on polished Brilliant Crios and Lava Ultimate (p ≥ 0.408). Grit blasted Tetric CAD showed no significant differences (p ≥ 0.096). The silane primer had minimal impact on grit blasted Tetric CAD (p ≥ 0.384). The silane primer increased the bond strength of OC7 to Brilliant Crios (p = 0.001) but decreased the adhesion of SBU to Brilliant Crios and Lava Ultimate (p ≤ 0.018). CONCLUSIONS: Bond strength of universal adhesives varied with CCRBC type. The two-component silane coupling agent showed mixed effects on adhesive performance. CLINICAL SIGNIFICANCE: Selecting universal adhesives from the same CCRBC product line does not always guarantee superior bond strength. The efficacy of silane coupling agents differs based on the bonding substrate.

How to optimize bonding procedures on healthy and hypomineralized enamel in orthodontics? / Comment optimiser les procédures de collage sur l'émail sain et hypominéralisé en orthodontie ?

Introduction: Bonding to enamel is a daily problem for the orthodontist. While bonding to healthy enamel is nowadays well mastered, bonding to hypomineralized enamel is much less so. The aim of this article was to help the orthodontist to optimise bonding, whatever the clinical situation. Material and Method: Based on data from the literature, the clinical and microscopic characteristics of healthy and hypomineralised enamel, including amelogenesis imperfecta (AI), molar incisor hypomineralization (MIH), fluorosis or erosion will be described. Proposals for optimising bonding will then be identified and summarized. Results: Bonding to enamel is reliable, but the use of an etch-and-rinse mode (even with a universal adhesive) is recommended. For AI, MIH and fluorosis, the use of sodium hypochlorite after etching seems to significantly increase bonding. No treatment is needed for eroded enamel. However, deep resin infiltration for severe MIH or superficial resin infiltration for fluorosis would reduce the risk of enamel fracture during bracket removal. Conclusion: It is important to be aware of the characteristics of the dental substrate and the materials used to optimize procedures.

Introduction: L'adhésion à l'émail est une problématique quotidienne de l'orthodontiste. Si le collage à l'émail sain est aujourd'hui maîtrisé, celui sur l'émail hypominéralisé l'est beaucoup moins. L'objectif de cet article était d'aider l'orthodontiste à optimiser son collage, quelle que soit la situation clinique. Matériel et méthode: À partir des données issues de la littérature, les caractéristiques clinique et microscopique de l'émail sain et de l'émail hypominéralisé en cas d'amélogenèse imparfaite (AI), d'hypominéralisation de molaire incisive (MIH), de fluorose ou d'érosion seront décrites. Puis, les propositions d'optimisation du collage seront recensées et synthétisées. Résultats: Le collage à l'émail est fiable, mais l'utilisation d'un mode mordançage-rinçage (même avec un adhésif universel) est conseillée. Pour l'AI, la MIH et la fluorose, l'utilisation d'hypochlorite de sodium après mordançage semble significativement augmenter l'adhérence. Aucun traitement n'est nécessaire pour l'émail érodé. Cela dit, une infiltration de résine en profondeur pour les MIH sévères ou superficielles pour la fluorose permettrait de réduire le risque de fracture d'émail à la dépose de l'attache. Conclusion: Il convient de connaître les caractéristiques du substrat sur lequel on colle et celles des matériaux utilisés pour optimiser ses procédures.

Description and Durability of the Various Indirect Restoration Techniques in Molar-Incisor Hypomineralisation: A Systematic Review.

Molar-incisor hypomineralisation (MIH) is a qualitative defect of the enamel structure. Indirect restorations may represent the most suitable therapeutic solutions for patients presenting MIH with tooth restorative procedures. This systematic review aims to determine the feasibility of indirect restorations. MATERIALS AND METHODS: A systematic review has been performed and is reported following the PRISMA guidelines. It was performed on three databases (PubMed, Science Direct, and Google Scholar). Ten articles were included. RESULTS: Only two articles reported the use of CAD/CAM technologies, whereas the other eight preferred conventional registration and handmade stratification for ceramics. All indirect bonded restorations made of composite resins or ceramics had significant success rates. A temporary material was placed in most of the articles. There was no clear consensus for tissue conditioning before bonding. Depending on the authors and the articles, the follow-up period extended from 2 months to 6 years. CONCLUSIONS: The survival rate and the non-invasive procedures of indirect restorations are two main arguments that can help dental practitioners in daily practice. Development of CAD/ CAM technologies adds new perspectives in the registration, the design and production. However, more clinical trials are needed to confirm the conclusions.

Comparative Evaluation of Application of Universal Bonding on the Microtensile Bond Strength of Light Cure and Dual Cure Composites Bonded to Dentin.

Objectives: There is limited knowledge on the efficacy of universal adhesives when used in different etching modes. The aim of this study was to evaluate the microtensile bond strength (µTBS) to dentin using universal adhesives with light-cure and dual-cure composites. Materials and Methods: In this in vitro experimental study, the occlusal third of 60 caries-free human molars were removed and the exposed surfaces were treated and allocated to 10 groups (N=6). Two different bonding agents (Single Bond Universal, G-Premio) were used to bond 2 different composite resins (Z250 light-cure and CoreFlo DC dual-cure) to dentin, using etch-and-rinse (E&R) and self-etch (SE) modes. Single Bond 2 was applied in E&R mode on wet dentin to serve as control. The specimens were sectioned into 1×1 mm2 sticks with a precision saw. A microtensile testing machine was used to measure the µTBS of the specimens with a crosshead speed of 0.5 mm/min. Data were analyzed using three-way ANOVA and Bonferroni post-hoc test (α=0.05). Results: The Single Bond Universal group in SE mode with light-cure composite yielded the highest (39.24MPa), and the G-Premio SE group with dual-cure composite produced the lowest (13.65MPa) mean µTBS (P<0.05). The dominant failure mode was adhesive, in all groups. Conclusion: The bonding agent had a significant effect on µTBS of composite to dentin, but different composites and different etching modes were not significantly different in this respect.

Evaluation of Er:YAG and Er,Cr:YSGG lasers on intraradicular bonding using modified glass fiber tips.

The aim of this study was to determine whether erbium laser irradiation emitted by modified glass-fiber tips would improve the intraradicular bonding of fiber posts. Forty human canines were endodontically treated and prepared for fiber-post placement. Roots were divided into five groups (n=8); according to the laser-tip combinations (2,940 nm Er:YAG and 2,780 nm Er,Cr:YSGG). Non-irradiated root canals served as control. Posts were cemented with self-adhesive resin cement and subjected to push-out test. Failure modes were characterized, and intraradicular bonded interfaces were analyzed by SEM and submitted to nanoleakage evaluation. Data were analyzed by two-way ANOVA and Tukey test (α=0.05). No significant differences were observed in cervical and middle sections (p>0.05), while significantly higher bond strengths were observed in apical sections (p<0.05). Laser irradiation reduced adhesive failures, cement-dentin gap formation, and nanoleakage apically. Laser-irradiation protocols employing end- or radial-firing tips improved bonding to apical intraradicular dentin contributing to more uniform bonded interfaces.

Current antibacterial agents in dental bonding systems: a comprehensive overview.

Dental caries is mainly caused by oral biofilm acid, and the most common dental restoration treatment is composite dental restorations. The main cause of failure is secondary caries adjacent to the restoration. Long-term survival of dental materials is improved by the presence of antibacterial agents, which selectively inhibit bacterial growth or survival. Chemical, natural and biomaterials have been studied for their antimicrobial activities and antibacterial bonding agents have been improved. Their usage has been increased to inhibit the growth of invading and residual bacteria in the oral cavity, as biofilm accumulation increases the risk of treatment failure. In this article, the success and applications of antibacterial agents are discussed in dental bonding systems.

Evaluation of repair bond strength of a dental CAD/CAM resin composite after surface treatment with two Er,Cr:YSGG laser protocols following artificial aging.

The aim of the present study was to evaluate the impact of two Er,Cr:YSGG laser surface treatments on the repair bond strength of a dental CAD/CAM resin composite (Brilliant Crios) after artificial aging. Twenty-four resin-based CAD/CAM blocks were cut and 48 rectangular slabs (3 x 12 x 14 mm) were prepared. Preliminary SEM observations indicated the most favorable laser settings regarding surface modification of the tested restorative material. The CAD/CAM specimens were then divided into 4 groups (n=12) based on their surface pretreatment: no treatment, air abraded with 50-µm Al2O3 particles, and laser irradiated with two different protocols using Er,Cr:YSGG laser with average power 3.5 and 4.5 W, pulse repetition rate 35 and 50 Hz, and pulse energy 100 and 90 mJ, respectively. After surface treatments each group followed a bonding protocol with silane and a flowable resin composite was used to prepare 48 microrods. Half of the microrods of each group were subjected on shear bond strength (SBS) test (chisel-shaped blade, load cell of 500 N, crosshead speed of 1 mm/min) after 24 h, while the other half underwent artificial aging (15,000 cycles, 5-55 °C) and then SBS test. The debonded specimens were examined under an optical microscope to determine the failure mode. All specimens were also evaluated using SEM to assess the surface topography after the treatments. The results showed that SBS significantly decreased after thermocycling in all the experimental groups (p<0.05). Control group presented much lower SBS values than the other groups after both 24 h and thermocycling (p<0.05). The highest values of SBS exhibited air-abrasion group (p<0.05), followed by the two laser groups, which did not differ to each other (p>0.05). The results of the current study indicated that Er,Cr:YSGG laser irradiation can be an alternative treatment for repairing the tested resin-based CAD/CAM restorative material.